A multijunction of ZnIn2S4 nanosheet/TiO2 film/Si nanowire for significant performance enhancement of water splitting

Nano Res. 2015. 11. 3524

Q. Liu, F. Wu, F. Cao, L. Chen, X. Xie, W. Wang, W. Tian*, L. Li*


Photoelectrodes with a specific structure and composition have been proposed for improving the efficiency of solar watersplitting. Here, a novel multijunctionstructure was fabricated, with Si nanowires as cores, ZnIn2S4 nanosheets as branches, and TiO2 films as sandwiched layers. This junction exhibited asuperior photoelectrochemical performance with a maximum photoconversion efficiency of 0.51%, which is 795 and 64 times higher than that of a bare Si wafer and nanowires, respectively. The large enhancement was attributed to the effective electron-hole separation and fast excited carrier transport within the multijunctions resulting from their favorable energy band alignments with water redox potentials, and to the enlarged contact area for facilitating the electron transfer at the multijunction/electrolyte interface.

首页 Home




联系我们

地址: 苏州大学本部 物理科技楼119房间

E-mail:

lli@suda.edu.cn  李老师

jeffni@suda.edu.cn 倪老师

wtian@suda.edu.cn 田老师

dkm@suda.edu.cn  邓老师