Engineering Bi2O3-Bi2S3heterostructure for superior lithium storage

Sci. Rep. 2015. 5. 9307

T. Liu, Y. Zhao, L. Gao*, J. Ni*


Bismuth oxide may be a promising battery material due to the high gravimetric (690 mAh g(-1)) and volumetric capacities (6280 mAh cm(-3)). However, this intrinsic merit has been compromised by insufficient Li-storage performance due to poor conductivity and structural integrity. Herein, we engineer aheterostructure composed of bismuth oxide (Bi2O3) and bismuth sulphide (Bi2S3) through sulfurization of Bi2O3 nanosheets. Such a hierarchical Bi2O3-Bi2S3 nanostructure can be employed as efficient electrode material for Li storage, due to the high surface areas, rich porosity, and unique heterogeneous phase. The electrochemical results show that the heterostructure exhibits a high Coulombic efficiency (83.7%), stable capacity delivery (433 mAhg(-1) after 100 cycles at 600 mAg(-1)) and remarkable rate capability (295 mAhg(-1) at 6 A g(-1)), notably out performing reported bismuth based materials. Such superb performance indicates that constructing heterostructure could be a promising strategy towards high-performance electrodes for rechargeable batteries.



首页 Home




联系我们

地址: 苏州大学本部 物理科技楼119房间

E-mail:

lli@suda.edu.cn  李老师

jeffni@suda.edu.cn 倪老师

wtian@suda.edu.cn 田老师

dkm@suda.edu.cn  邓老师